CONVERSION OF INDUCTION HEATING DEPOSITED MONETITE COATING TO HYDROXYAPATITE COATING ON HT–C/C COMPOSITES BY HYDROTHERMAL TREATMENT IN KOH AQUEOUS/AMMONIA SOLUTION

Carbon/carbon composites with hydroxyapatite coatings are one of the attractive materials in the dental and orthopedic fields. In this study, hydrothermal treatment, in KOH aqueous and ammonia solutions, was used to convert an induction-heating-deposited monetite coating to an adherent HA coating on H2O2 treated C/C composites. The structure, morphology and chemical composition of the as-received HA coatings were characterized by XRD, FTIR, SEM and EDS. A scratch test was conducted to measure the adhesion of HA coatings to HT–C/C substrate. The results show that well-crystallized carbonate hydroxyapatite coatings could be achieved under the two reaction mediums. However, the as-obtained HA coatings after KOH hydrothermal treatment have higher crystallinity and Ca/P ratio than those after ammonia hydrothermal treatment, and reveal an average critical load of 29 N which is more than two times as high as that for HA coatings after ammonia hydrothermal treatment.