PREPARATION AND FERROELECTRIC PROPERTY OF (100)-ORIENTED Ca0.4Sr0.6Bi4Ti4O15 THIN FILM ON Pt/Ti/SiO2/Si SUBSTRATE

The (100)-oriented Ca0.4Sr0.6Bi4Ti4O15(C0.4S0.6BTi) thin film was successfully prepared by a sol-gel method on Pt/Ti/SiO2/Si substrate. The orientation and formation of thin films under different annealing schedules were studied using XRD and SEM. XRD analysis indicated that (100)-oriented C0.4S0.6BTi thin film with degree of orientation of I(200)/I(119) = 1.60 was prepared by preannealing the film at 400°C for 3 min followed by rapid thermal annealing at 800°C for 5 min. SEM analysis further indicated that the (100)-oriented C0.4S0.6BTi thin film with a thickness of about 800 nm was mainly composed of equiaxed grains. The remanent polarization and coercive field of the film were 16.1 μC/cm2 and 85 kV/cm, respectively.