Carbon Foam -Reinforced Polyimide-Based Carbon Aerogel Composites Prepared Via Co-Carbonization as Insulation Material

The weak inherent non-covalent interactions between carbon aerogel backbone nanoparticles obtained by pyrolysis of conventional organic aerogel can lead to poor mechanical properties. When applied in thermal protection system of high-speed spacecraft, the preparation of carbon aerogel insulation materials with excellent formability and high mechanical strength still remains a huge challenge. This work reports an efficient approach for fabricating carbon foam-reinforced carbon aerogel composites by compounding the nano-porous polyimide aerogel into the micro-porous pre-carbonized phenolic resin-based carbon foam via vacuum impregnation, gelatinizing and co-carbonization. Benefiting from the co-shrinkage caused by co-carbonization, the thermal insulation capacity of the carbon aerogel and the formability of the pre-carbonized foam are efficiently utilized. The shrinkage, density, carbon yield of aerogels, pre-carbonized foams and the composites at different temperatures were measured to analyze the formation of the interfacial gap within the composite. The co-carbonization mechanism of the polyimide aerogels and phenolic resin-based pre-carbonized foams was analyzed through XPS, TG- MS, and FT-IR. Among the prepared samples, CF30-CPI-1000 °C with small interfacial gaps showed the lowest thermal conductivity, which was as low as 0.56 W/(m•K) at 1900°C, and the corresponding compressive strength and elastic modulus were as high as 0.532 MPa and 9.091 MPa, respectively