SYNTHESIS OF HIGHLY CRYSTALLINE OLIVINE-TYPE LiFePO4 NANOPARTICLES BY SOLUTION-BASED REACTIONS

LiFePO4 nanocrystals were synthesized in various polyol media without any further post-heat treatment. The LiFePO4 samples synthesized using three different polyol media namely, diethylene glycol (DEG), triethylene glycol (TEG), and tetraethylene glycol (TTEG), exhibited plate and rod-shaped structures with average sizes of 50–500 nm. The X-ray diffraction (XRD) patterns were indexed on the basis of an olivine structure (space group: Pnma). The samples prepared in DEG, TEG, and TTEG polyol media showed reversible capacities of 123, 155, and 166 mAh/g, respectively, at current density of 0.1 mA/cm2 with no capacity fading and exhibited excellent capacity retention up to the 50th cycle. In particular, the samples showed excellent performances at high rates of 30 and 60 C with high capacity retention. It is assumed that the nanometer size materials (~50 nm) possessing a highly crystalline nature may generate improved performance at high rate current densities.