Epitaxial growth and magnetic exchange anisotropy in Fe3O4<Emphasis Type="Bold">/NiO bilayers grown on MgO(001) and Al2O3(0001)

Epitaxial Fe3O4/NiO bilayers were epitaxially grown on MgO(001) and Al2O3(0001) substrates to investigate the influence of the fully spin compensated (001) and the non-compensated (111) NiO interface planes between the ferromagnetic (F) and antiferromagnetic (AF) layers on the AF/F exchange coupling. Bilayers of different magnetite thicknesses and constant NiO thickness were investigated. The structural characterizations indicate a perfect epitaxy of the two layers for the both growth directions in the two Fe3O4/NiO/MgO(001) and NiO/Fe3O4/Al2O3(0001) systems. An epitaxial ferrimagnetic (Ni,Fe)Fe2O4 phase is observed at the AF/F  interface when the NiO oxide is grown on the top of the Fe3O4 layer while a perfectly flat AF/F interface is observed in the Fe3O4/NiO/MgO(001) system exhibiting only a very slight interdiffusion. Magnetic measurements indicate a relative strong bias at 300 K for the bilayers grown on Al2O3(0001), which decreases with the inverse of the ferrimagnetic layer thickness as theoretically expected. On the contrary, a zero exchange biasing is observed at 300 K for the bilayers grown on MgO(001). Copyright EDP Sciences/Società Italiana di Fisica/Springer-Verlag 2005